Fibre-reinforced, quick setting and hardening, compensated-shrinkage mortar for repairing concrete. TECHNICAL DATA: Maximum dimension of aggregate: 1 mm. Mixing ratio: 100 parts of MAPEGROUT FAST-SET…
Fibre-reinforced, quick setting and hardening, compensated-shrinkage mortar for…
Hi-flow, steel fibre-reinforced compensated-shrinkage, quick-setting and hardening, high-ductility cementitious mortar applied at temperatures down to -5°C, with stiff steel fibres for repairing…
Medium-strength (40 MPa), compensated-shrinkage fibre-reinforced thixotropic mortar for repairing concrete. TECHNICAL DATA: Maximum dimension of aggregate: 2.5 mm. Mixing ratio: 100 parts of…
Fibre-reinforced, sulphate-resistant thixotropic mortar for repairing concrete. TECHNICAL DATA: Maximum dimension of aggregate: 2.5 mm. Mixing ratio: 100 parts of MAPEGROUT T60 with 16.5-17.5 parts…
Fibre-reinforced, sulphate-resistant thixotropic mortar for repairing concrete.…
Fibre-reinforced, compensated-shrinkage mortar for repairing concrete. TECHNICAL DATA: Maximum dimension of aggregate: 2.5 mm. Mixing ratio: 100 parts of MAPEGROUT TISSOTROPICO with 15.5-16.5 parts…
Fibre-reinforced, compensated-shrinkage mortar for repairing concrete.…
Pre-impregnated alkali-resistant A.R. glass fibre mesh (FRP) used to make “reinforced” structural render on concrete and masonry structures. TECHNICAL DATA: Type of fibre: A.R. type glass fibre.…
Pre-impregnated alkali-resistant A.R. glass fibre mesh (FRP) used to make…
High tensile pultruded carbon fibre rebars impregnated with epoxy resin for structural strengthening of damaged concrete, wooden and masonry elements. TECHNICAL DATA: Modulus of elasticity: 155,000…
High tensile pultruded carbon fibre rebars impregnated with epoxy resin for…
Pultruded glass fibre rebar pre-impregnated with epoxy-modified vinylester resin for structural reinforcement of damaged reinforced concrete, brick, stone and tuff elements. TECHNICAL DATA: Tensile…
Pultruded glass fibre rebar pre-impregnated with epoxy-modified vinylester…